FEATURES
-
Excellent Resistance to Heavy Impact and
gets work hardened.
-
Particularly suitable for rebuilding,
reclamation of heavy parts made of
carbon or 14% Mn - steel.
-
High metal recovery 80 to 85 %.
-
High Deposition rate, No slag removal,
Non-hygroscopic coating, No pre-drying
and Longer shelf-life.
TYPICAL APPLICATIONS
: Buffer layers on worn out components of
Manganese steels.
ALLOY BASIS
: C, Mn, Ni. STRUCTURE
: Weld-metal contains Austenitic Manganese
steel deposit.
HARDNESS
: As Welded 22 to 25 Rc. / Work hardened
to 48 to 50 Rc.
RECOMMENDED CURRENT
: DC (+) Preferred / AC 70 OCV
|
Size (mm)
|
Amps
|
|
6.30 x 450
|
75 to 130
|
|
8.00 x 450 |
110 to 160 |
|
10.00 x 450 |
130 to 180 |
IDENTIFICATION
: Tip Color - GOLD
Note : Weld-Metal
being rich in Mn is sluggish in nature.
Hence, Nominal weaving / Stringer bead is
preferred. |