FEATURES
-
Chrome Manganese Electrode having
Excellent Work Hardening Properties.
-
Resistance to Impact accompanied with
Abrasion.
-
General purpose joining, surfacing and
buttering.
-
Crack free thick deposit for rebuilding,
reclamation of heavy parts made of Mn
steel or Carbon Steel.
-
Weld-metal recovery is as high as 80 to
85 %.
-
High Deposition rate, No slag removal,
Non-hygroscopic coating and No
pre-drying.
-
Longer shelf-life.
TYPICAL
APPLICATIONS : Railway points & crossings,
crusher jaws, crusher hammers, blow bars,
toothed crusher rolls, swing hammers,
crusher mantles etc. ALLOY BASIS
: C, Mn, Cr
STRUCTURE
: Weld-metal is composed of Cr-rich Austenitic deposit.
HARDNESS
: As welded : 25 to 30 Rc. / Work hardened
upto : 50 to 52 Rc. RECOMMENDED CURRENT
: DC (+) Preferred / AC 70 OCV
|
Size (mm)
|
Amps
|
|
6.30 x 450
|
75 to 130
|
|
8.00 x 450 |
110 to 160 |
|
10.00 x 450 |
130 to 180 |
IDENTIFICATION
: Tip Color - PINK
Note : Weld-Metal
being rich in Mn is sluggish in nature.
Hence, Nominal weaving / Stringer bead is
preferred.
|