FEATURES
-
Excellent Abrasion Resistance under Low
to Moderate Impact.
-
Particularly suitable for Wear Resistant
Overlays on Austenitic Manganese steels.
-
Can
also be used on Carbon & Alloy steel.
-
Weld-metal recovery is as high as 80 to
85 %.
-
High Deposition rate, No slag removal,
Non-hygroscopic coating and No
pre-drying.
-
Longer shelf-life.
TYPICAL
APPLICATIONS : Bucket lips & teeth,
primary coal crushing jaws & hammers, quarry
screen plates, blow bar, mantles & liners,
gyratory and cone crusher parts, etc.
ALLOY BASIS
: C, Cr.
STRUCTURE
: Weld-metal contains large quantities of
Chromium Carbides in tough Matrix of
Austenite.
HARDNESS
: Single Layer 52to 56 Rc. / Two Layers 58
to 61 Rc.
RECOMMENDED CURRENT
: DC (+), AC 70 OCV
|
Size (mm)
|
Amps
|
|
6.30 x 450
|
75 to 130
|
|
8.00 x 450 |
110 to 160 |
|
10.00 x 450 |
130 to 180 |
IDENTIFICATION
: Tip Color - MINT GREEN
Surface Relief-Checks in weld-metal are
normal and infact, desirable. These checks
prevent stress build-up because of high
hardness and high-alloy contents. |